·TA75K-FD-10是一款高性能材料，具有非常强劲的包胶粘接强度和特别舒适的手感。可快速成型。

·TA75K-FD is a kind of high performance material which has very strong adhesive strength and special comfortable touch.Also it can be taken shape rapidly.

关键特性Key characteristic

1.表面哑，手感细腻爽滑。Dumb surface, the handle is exquisite and smooth

2.粘接强度非常高,可粘接材质:ABS.PC TPU。Very high bonding strength, adhesive materials：ABS,PC,TPU.

3.成型快、不粘模具。Rapid molding，non-stick mold

4.表面耐刮擦，不易起毛屑。Scratch resistance on the surface,not easy to fluff

功能Function

产品应用

Main application

手机保护Phone protective cover

电脑Computer

仪器外壳Instrument shell

电子器件粘胶配件Electronic plastic accessories

加工方法Processing method

1 注塑成型Injection molding     2 挤出成型Extrusion molding

环保认证

Environmental certification

ROHS

REACH

EN71-3

PAHS

ASTM-F963

Phthalate

颜色Color

本色 Natural

气味Smell

少许树脂味A little resin smell

外型Appearance

圆球形小颗粒Cylindrical particle，about 3mm×1.5mm

储藏期Storage period

常温下通风干燥，24个月Ventilated dry at normal temperature，about 24 months

包装方式Packaging method

25公斤/袋 25kg/bag

物理性能Physical properties

结果Result

单位Unit

方法Method

成型条件Molding condition

比重Specific gravity

1.15±0.02

g/cm3

ASTM D792

干燥温度Drying temp       90℃

硬度Hardness

70±5

shoreA

ASTM D2240

干燥时间Drying time     2Hours

拉伸强度Tensile strength

11±2

Mpa

ASTM D412

射嘴温度Nozzle temp      180℃

断裂延伸Elongation at break

800±100

%

ASTM D412

螺筒一段温度Screw 1 temp 170℃

撕裂强度Tearing strength

48±5

Kn/m

ASTM D624

螺筒二段温度Screw 2 temp 160℃

熔融指数Melt index

30±6

g/10min

ASTM D1238

螺筒三段温度Screw 3 temp 160℃

注意事项Matters need attention

清洗料管

Purge compound

需使用PP或 PE清洗干净机台螺杆，且把机台射嘴彻底清除干净please make sure you that you have cleaned the machine screw with PP or PE, and put the machine nozzle thoroughly clean

着色

Coloring

请选择以PE或EVA为基材之色母，切勿使用以PVC为基材者。另外加工时请采用较高的螺杆转速和较高的背压，才能让着色剂达到较好的分散效果Please select color master batch on PE or EVA material with the exception of PVC.Higher screw speed and backpressure and needed for better colorant dispersion

回收Recycling

二次料（水口料）回收比率建议最多10%。Consistent regrind usage of up to 10% is permissible